READY TO SPRAY | 4.2 VOC
FEATURES:
A single component primer formulated to improve topcoat adhesion on bare metal, galvanized steel, stainless steel, aluminum and other substrates.
 
• Provides maximum adhesion and corrosion
resistance on all types of bare metal
• Can be used on steel, aluminum and
galvanized steel
• 1-2 medium wet coats
DRY TIMES:
• Allow 30 minutes @ 70°F (21°C) air
dry before priming. Total milage should
be 0.5 to 0.75 mil.
SANDING:
• Can be primed without sanding. If Primer is not primed within 16 hours it should be sanded with 180-240 grit sandpaper
PRIMER: DI-1KSEP (GALLON)
​
​
PART NUMBER INFORMATION:
 
​
1K SELF ETCHING PRIMER
GUN SETUP:
• Gravity: 1.3mm-1.4mm 40-45 psi @ gun
• Siphon 1.3mm-1.4mm 40-45 psi @ gun
• HVLP 1.3mm-1.4mm 8-10 psi @ gun
PRIMERS
DI LOGO.png
SELF ETCHING PRIMER
1:1 MIX | 4.2 VOC
GUN SETUP:
• Gravity: 1.3mm-1.4mm 40-45 psi @ gun
• Siphon 1.3mm-1.4mm 40-45 psi @ gun
• HVLP 1.3mm-1.4mm 8-10 psi @ gun
FEATURES:
An acid-based, etching primer designed to optimize adhesion to bare metal substrates and provide a corrosion resistant barrier between substrate and coatings.
 
• 2 Part coating
• Designed to give maximum adhesion and
corrosion resistance on, Lacquer Primer Surfacer,
Epoxy Primer Sealer, 2K Urethane Sealer
• 1-2 Medium wet coats
DRY TIMES:
• Allow 30 minutes @ 70°F (21°C) air
dry before priming
SANDING:
• Can be primed without sanding. If Primer is not primed within 16 hours it should be sanded with 180-240 grit sandpaper
PART NUMBER INFORMATION:
PRIMER: DI-SEP (QUART)
ACTIVATOR: DI-SEPA (8oz)
LACQUER PRIMER
4:1 MIX | 2.1 VOC
GUN SETUP:
• Gravity: 1.6mm-1.8mm 40-45 psi @ gun
• Siphon 1.6mm-1.8mm 40-45 psi @ gun
• HVLP 1.6mm-1.8mm 8-10 psi @ gun
FEATURES:
A premium quality acrylic lacquer primer for use in automotive applications. It is formulated with the highest quality resins
 
• Very fast dry time; sand in approximately 30
minutes
• Excellent adhesion to cured finishes, body filler and sanded fiberglass
• Superior filling and sanding properties
• 2-3 Full wet coats
SANDING
• Allow to thoroughly dry before sanding.
 
Finish sand as follows:
• Sealer | 320-400 grit
• Single-stage system | 320-400 grit
• Basecoat | 400-500 grit
DRY TIMES:
• Sand in approximately 30 minutes
PART NUMBER INFORMATION:
BLACK PRIMER: DI-LPB (GALLON & QUART)
GRAY PRIMER: DI-LPG (GALLON & QUART)
ACTIVATOR: ZERO VOC REDUCER OR ACETONE
EPOXY PRIMER
1:1 MIX | 4.2 VOC
GUN SETUP:
• Gravity: 1.6mm-1.8mm 40-45 psi @ gun
• Siphon 1.6mm-1.8mm 40-45 psi @ gun
• HVLP 1.6mm-1.8mm 8-10 psi @ gun
FEATURES:
A fast-dry epoxy with excellent corrosion resistance and adhesion to a variety of properly prepared metals and some automotive plastics.
 
• Can be directly topcoated, wet-on-wet, with any topcoat system
• Fast dry, fast curing epoxy that has excellent
corrosion resistance and adhesion
• Can be used as a primer surfacer or a sealer
• Tintable
• 1-2 Full wet coats
PART NUMBER INFORMATION:
BLACK PRIMER: DI-EPB (GALLON & QUART)
GRAY PRIMER: DI-EP (GALLON & QUART)
ACTIVATOR: DI-EPA (GALLON & QUART)
SUBSTRATES:
• Clean, sanded fiberglass or SMC
• Clean, sanded OEM finishes
• Clean, sanded cured aftermarket finishes
• Autobody fillers
DRY TIMES:
• Topcoated in 30-60 minutes @ 72ËšF (22.2ËšC)
• Allow 60-90 minutes @ 70ËšF (21ËšC) cure
time before applying polyester body filler
DIRECT TO METAL PRIMER
4:1 MIX | 2.1 VOC
GUN SETUP:
• Gravity: 1.6mm-1.8mm 40-45 psi @ gun
• Siphon 1.6mm-1.8mm 40-45 psi @ gun
• HVLP 1.6mm-1.8mm 8-10 psi @ gun
FEATURES:
A two-component primer surfacer that has excellent adhesion to cold-rolled steel, aluminum, galvanized panels, galvanneal, body filler, fiberglass, SMC and OEM finishes.
 
• Has excellent anti-corrosion properties and sands
easily without loading the sandpaper.
• Eliminates the need for pre-treatment primer
• Easily sprays and levels with little overspray
• 2-3 Full wet coats
DRY TIMES:
AIR DRY
• Dry to Sand 90 minutes
• Flash Between Coats 10-15 minutes

 
EXPRESS DRY
• Flash between coats 10-15 minutes
• Flash before force dry (Purge Time)
10 minutes
• Cycle Time 15-20 minutes@140F
PART NUMBER INFORMATION:
DTM PRIMER: DI-DTM (GALLON) DI-DTM-Q (QUART)
ACTIVATOR: DI-DTMA (QUART) DI-DTMA-8OZ (8oz)
2K URETHANE PRIMER
4:1 MIX | 4.2 VOC
GUN SETUP:
• Gravity: 1.7mm-1.8mm 40-45 psi @ gun
• Siphon 1.7mm-1.8mm 40-45 psi @ gun
• HVLP 1.7mm-1.8mm 8-10 psi @ gun
FEATURES:
A two-component primer surfacer that has excellent adhesion to cold-rolled steel, aluminum, galvanized panels, galvanneal, body filler, fiberglass, SMC and OEM finishes.
 
• Has excellent anti-corrosion properties and sands
easily without loading the sandpaper.
• Eliminates the need for pre-treatment primer
• Easily sprays and levels with little overspray
• 2-3 Full wet coats
DRY TIMES:
• Air Dry: Dry to Sand 1-1/2 to 2 hours
• Express Dry: Cycle Time IR 15-20 minutes
SANDING:
DRY SANDING
• Initial Sanding180-220 grit
• Finish Sanding 320-400 grit

 
WET SANDING
• Finish Sanding 320-400 grit
PART NUMBER INFORMATION:
PRIMER: DI-2KP (GALLON & QUART)
ACTIVATOR: DI-2KPA (QUART & 8oz)
ACID ETCH PRIMER
FEATURES:
A dual-purpose, high-build specialty coating
designed for priming and surfacing of metal and plastic parts. This primer helps prevent rust and seals out moisture while providing a base for topcoating.

 
• Must be topcoated with another primer before topcoating with polyester-based coatings.
• 2 coats at a distance of approx. 10 inches from the surface.
• 20oz. Aerosol can
INSTRUCTIONS
• Shake the aerosol can for at least 2 minutes before use.
• For best results, ensure the surface is thoroughly cleaned, degreased, dried and dust free. Abrade primed surfaces wet or dry with P180 - P220 grit sandpaper,
degrease and dry.
READY TO SPRAY | 4.2 VOC
SUBSTRATES
• Bare steel
• Aluminum
• Galvanized and zinc coated steels
• Polyester bodyfillers and GRP
• Fully cured paint
FLASH OFF
• 3-5 minute flash between coats
DRY TIMES
• Drying Times: 3-5 mins between coats @ 68°F
PRIMER: DI-741
​
​
PART NUMBER INFORMATION:
 
​
HIGH BUILD PRIMER
READY TO SPRAY | 4.2 VOC
FEATURES:
A dual-purpose, high-build specialty coating
designed for priming and surfacing of metal and plastic parts. This primer helps prevent rust and seals out moisture while providing a base for topcoating.

 
• Excellent flexibility and adhesion so it can be
applied on both flexible and rigid parts.
• Dries fast, has excellent build and is easy to sand.
• Paintable in 20 minutes.
• 20oz. Aerosol can
TECHNICAL NOTES:
• Compatible with All basecoat systems
• Designed to powerfully adhere to both plastic and metal
SUBSTRATES:
• Direct to Metal
• SMC
• Lighty abraded E-Coat
• Fiberglass
• OEM paint surfaces
FLASH TIMES:
• 5-10 mins between coats
DRY TIMES:
• Sand and topcoat in 20 minutes or less
SANDING:
• Dry Sanding: P400-P600
• Wet Sanding: P600-P800
DI HIGH BUILD.png
PART NUMBER INFORMATION:
 
​
MEDIUM GRAY: DI-791
DARK GRAY: DI-765
WHITE: DI-763
BLACK: DI-764
​
​
​
bottom of page